Influence of Electroplating Time on the Hardness Properties of Nickel-Coated Aluminum

Margono Margono, Cavin Dwi Prasetyo, Moch Chamim, Deni Andriyansyah, Bondan Wiratmoko Budi Santoso, Deslana Avinda Krisna Putra, Arif Surono, Hassan Khamis Hassan

Abstract


This study investigates the effect of electroplating duration on the hardness and coating thickness of nickel layers deposited on aluminum substrates. Nickel electroplating was performed with immersion times of 17, 34, 51, and 68 min to evaluate the correlation between deposition time, microstructural development, and mechanical enhancement. Microstructural analysis revealed a progressive increase in coating thickness from 3 μm, 7 μm, 11 μm, to a maximum of 44 μm as plating duration increased. Correspondingly, surface hardness exhibited a substantial rise, with untreated aluminum showing 69.44 HV, while electroplated specimens achieved 118.32 HV, 191.32 HV, 258.40 HV, and 418.62 HV, respectively. This increase of up to 502% demonstrates that longer electroplating durations produce denser and finer nickel microstructures, contributing significantly to surface strengthening. The findings confirm that nickel electroplating is an effective method for enhancing the mechanical performance and surface quality of aluminum, with deposition time serving as a critical parameter in optimizing coating characteristics.


Full Text:

PDF

References


Krim S, Giljean S, Marsiquet C, et al. Annealing of Electrodeposited Nickel Coatings on Aluminum Alloy: Microstructural Properties and Wear Resistance of Nickel-Rich Aluminide Layers. J Mater Eng Perform 2024;33:10712–25. https://doi.org/10.1007/s11665-023-08719-2.

Rosyidan C, Soegijono B, Kurniawan B. Effect of nickel electroplating process time variation over aluminum on crystalplane orientation. AIP Conf Proc 2023;2598:40009. https://doi.org/10.1063/5.0126191.

Joseph A, Narayanasamy M, Kirubasankar B, et al. Development of MoS 2 Nanosheets Embedded Nickel Composite Coating and its Mechanical Properties. ES Mater Manuf 2018;2:2–8. https://doi.org/10.30919/esmm5f152.

Sherwin C, Bhat S, Hebbar SP. Effect of plating time on surface morphology and coating thickness of nickel plating on copper surface. J Phase Chang Mater 2021;1.

Mascenik J, Coranic T, Kuchar J, et al. Influence of Selected Parameters of Zinc Electroplating on Surface Quality and Layer Thickness. Coatings 2024;14:1–20.

Emanuele R, Comparini A, Verrucchi M, et al. Nickel release from 316L stainless steel following a Ni-free electroplating cycle. Heliyon 2024;10:e37125.

Fajria H, Setiawan F, Wicaksono D. The Effect of Nickel Electroplating Time on Aluminum 2024 to Its Mechanical Property. J Mater Sci Geophys Instrum Theor Phys 2023;6:1–8.

Akhyar, Yaqin RI, Jalil Z. Surface Roughness and Hardness Characteristic of 2024 Aluminum Alloy by Electroplating Ni-Cr. J Phys Conf Ser 2021;2000:012009. https://doi.org/10.1088/1742-6596/2000/1/012009.

Khiabani A, Seyedraoufi Z-S, Sohi MH. Effect of heat treatment on surface characteristics and corrosion behavior of nickel plated AA2024 aluminum alloy. Surf Topogr Metrol Prop 2021;9:35048. https://doi.org/10.1088/2051-672X/ac19a0.

Riyadi TWB, Sarjito, Anggono AD, et al. Effect of Ni underlayer thickness on the hardness and specific wear rate of Cu in the laminated Ni/Cu coatings produced by electroplating. AIP Conf Proc 2018;1977. https://doi.org/10.1063/1.5042970.

Riyadi TWB, Masyrukan. Hardness and wear properties of laminated Cr-Ni coatings formed by electroplating. AIP Conf Proc 2017;1831:020034–6. https://doi.org/10.1063/1.4981175.

Yang-tao X, Yu-jie D, Wei Z, et al. Microstructure and texture evolution of electrodeposited coatings of nickel in the industrial electrolyte. Surf Coat Technol 2017;330:170–7. https://doi.org/10.1016/j.surfcoat.2017.09.078.

Li B, Li D, Chen W, et al. Effect of current density and deposition time on microstructure and corrosion resistance of Ni-W / TiN nanocomposite coating. Ceram Int 2019;45:4870–9. https://doi.org/10.1016/j.ceramint.2018.11.184.

Mohammed HK, Abbas AS, Mustafa AM. Characteristics and properties of bright nickel plated on aluminum substrate type AA - 1100. AIP Conf Proc 2024;3002:80030. https://doi.org/10.1063/5.0206370.

Sarp Y, Usta İ, Tan S, et al. Effect of Deposition Time on Hardness and Corrosion Properties of Electroless Nickel-Boron Coatings 2022:88–93. https://doi.org/10.31590/ejosat.1173924.

Rahimi A, Sarraf S, Soltanieh M. Nickel electroplating of 6061-T6 aluminum alloy using anodizing process as the pretreatment. J Mater Res Technol 2023;27:5701–8. https://doi.org/10.1016/j.jmrt.2023.10.285.

Juskowiak-Brenska A, Lapinski J, Pletcher D, et al. Porosity of nickel electrodeposits on mild steel using electrochemical impedance spectroscopy. Trans Inst Met Finish 2012;90:156–60.

Bahrololoom ME, Sani R. The influence of pulse plating parameters on the hardness and wear resistance of nickel – alumina composite coatings 2005;192:154–63. https://doi.org/10.1016/j.surfcoat.2004.09.023.

Wasekar NP, Haridoss P, Seshadri SK, et al. Influence of mode of electrodeposition , current density and saccharin on the microstructure and hardness of electrodeposited nanocrystalline nickel coatings. Surf Coat Technol 2016;291:130–40. https://doi.org/10.1016/j.surfcoat.2016.02.024.

Amanina N, Omar B, Frank K, et al. Texture orientation , morphology and performance of nanocrystalline nickel coatings electrodeposited from a Watts-type bath : Effects of H 3 BO 3 concentration and plating time. Surf Coat Technol 2021;424:127648. https://doi.org/10.1016/j.surfcoat.2021.127648.

Qiang J, Jiang B, Dong Y, et al. Tuning residual stress in electrodeposited nickel films via pulse current. Surfaces and Interfaces 2023;40:103038. https://doi.org/10.1016/j.surfin.2023.103038.

Meinhold V, Höhlich D, Mehner T, et al. Electrodeposition of Thick and Crack-Free Fe-Cr-Ni Coatings from a Cr ( III ) Electrolyte. Coatings 2022;12:1–15. https://doi.org/https://doi.org/10.3390/coatings12010056.

Thompson GW, Mahtabi MJ. Electrodeposition of Nickel onto Polymers : A Short Review of Plating Processes and Structural Properties. Appl Sci 2025;15:1–16.

Fattah M, Morin S. Microstructure, Corrosion, and Hardness Properties of Ni Coatings Electrodeposited from a Deep Eutectic Solvent-Based Electrolyte. J Mater Eng Perform 2025;34:18560–76. https://doi.org/10.1007/s11665-024-10565-9.

Guan T, Zhang N. Recent Advances in Electrodeposition of Nickel ‑ Based Nanocomposites Enhanced with Lubricating Nanoparticles. Springer Nature Singapore; 2024. https://doi.org/10.1007/s41871-024-00245-6.

Awasthi S, De S, Pandey SK. Heliyon Electrodeposited carbon nanostructured nickel composite coatings : A review. Heliyon 2024;10:e26051. https://doi.org/10.1016/j.heliyon.2024.e26051.

Van Hau T, Van Trinh P, Van Tu N, et al. Electrodeposited nickel–graphene nanocomposite coating: influence of graphene nanoplatelet size on wear and corrosion resistance. Appl Nanosci 2021;11:1481–90. https://doi.org/10.1007/s13204-021-01780-0.

Trabelsi D, Nasri F, Kharrat M, et al. Structural Characterization of Electrodeposited Ni Coatings Filled with Graphite or MoS2 Particles. Lect. Notes Mech. Eng., Cham: Springer Nature Switzerland; 2024, p. 249–57. https://doi.org/10.1007/978-3-031-57324-8_27.

Zhang Z, Wang H, Ma W, et al. Electrodeposition of Copper-Based Nickel – Graphene Coatings : Effect of Current Density on Microstructure and Properties. Coatings 2025;15:1–17. https://doi.org/https://doi.org/10.3390/coatings15121360.




DOI: https://doi.org/10.31284/j.jmesi.2026.v6i1.8767

Refbacks

  • There are currently no refbacks.


Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

Published by:
Institut Teknologi Adhi Tama Surabaya, Indonesia

Editorial Address
Journal of Mechanical Engineering, Science, and Innovation is licensed under CC BY-NC 4.0