ANALYSIS OF PRE-HEATING TEMPERATURE EFFECT ON SHIELDED METAL ARC WELDING (SMAW) OF BKI GRADE (KI-A) PLATES TO THE TENSILE STRENGTH AND HARDNESS

Erifive Pranatal, Noveta Fernaldinatan, Norita Prasetya Wardhani, Adi Kurniawan Yusim

Abstract


This study aimed to analyze BKI Grade (KI-A) plate material using the pre-heat process to determine tensile strength and hardness. The method involved welding with shielded metal arc welding (SMAW) type. The pre-heat variations used several temperatures, such as 50⁰C, 120⁰C, 220⁰C, and without heat treatment. The tensile strength obtained specimen without pre-heating had the lowest tensile strength of 442.64 MPa, and the specimen with pre-heating to 220⁰C had the highest average tensile strength of 450.11 MPa. The result showed that tensile strength was proportional to the pre-heating temperatures given. The hardness observation found that the hotter the pre-heating temperature obtained, the higher the hardness value of the base metal and HAZ would obtain. It was different with weld metal which would decrease. From those two parameters, it could be concluded that the most optimal pre-heat temperature was 220⁰C.


Full Text:

PDF

References


Waaddulloh, M., Sulardjaka, S., dan Dwi Haryadi, G. 2020. Pengaruh Arus dan Tegangan Pengelasan SMAW Baja Karbon Rendah Grade A dan Baja Karbon Rendah Grade B terhadap Sifat Mekanik. JMPM (Jurnal Material dan Proses Manufaktur), 4(2), 103–114. https://doi.org/10.18196/jmpm.v4i2.11450

Wiryosumarto, H Dan Okumura, T. 2000. Teknologi Pengelsan Logam. Cetakan Ke 8. Pradnya Paramita. Jakarta.

Wiyono, T., 2012. Penentuan Pengelasan Dissimiliar Allumunium Dan Pelat Baja Karbon Rendah Dengan Variasi Waktu Pengelasan Dan Arus Listrik. Jurnal Foundry Vol. 2 No. 1 April 2012 ISSN 2087-2259 :20 – 25.

Anggraeni, Safira Dwi., Pratikno, Herman., Setyo Hadiwidodo, Yoyok. 2016. “Studi Perbandingan Proses Pengelasan SMAW Pada Lingkungan Darat dan Bawah Air Terhadap Ketahanan Uji Bending Weld Joint Material A36”. Surabaya: Institut Teknologi Sepuluh Nopember (ITS).

Sukaini, T., dan Fandi, 2016. Teknik Las SMAW, edisi pertama, Kementerian Pendidikan & Kebudayaan Direktorat Jenderal Peningkatan Mutu Pendidik & Tenaga Kependidikan Sukmadinata, (2017), Metode Penelitian Pendidikan, Bandung: PT Remaja Rosdakarya

Mizhar, S., dan Pandiangan, I. H, 2014. Pengaruh Masukan Panas Terhadap Struktur Mikro, Kekerasan dan Ketangguhan pada Pengelasan Shielded Metal Arc Welding (SMAW) dari Pipa Baja Diameter 2,5 inch. Jurnal Dinamis, II (14), 16–22.

Joko S., (2006), Pengaruh Arus Pengelasan Terhadap Kekuatan Tarik Dan Ketangguhan Las Smaw Dengan Elektroda E7018, Jurnal Teknik Mesin UNES Vol, III, NO 11, 22 September 2006 ISSN 2102- 7491: 206 – 220

Windu Baskoro Hadi. 2015. “Analisis Pengaruh Variasi Temperatur Preheat terhadap Distorsi, Lebar HAZ, dan Struktur Mikro padaSambungan Butt Joint Single V dengan Metode Pengelasan FCAW dan SMAW”. Surabaya: Institut Sepuluh November. Windu Baskoro Hadi. 2015.

AWS, 2000. Structural Welding Code Steel, AWS Standard, Vol. D1.1.

Scott, F. 2000. Taking Your Weld’s Temperature. Jurnal Modern Steel Construction

Alip, M. 1989. Teori Dan Praktik Las. Departemen Pendidikan Dan Kebudayaan.

Firmansyah. 2020. “Tensile Test: Pengertian, Prosedur, Acceptance dan Standard” diakses pada 13 Januari 2022 https://www.detech.co.id/tensile-test/




DOI: https://doi.org/10.31284/j.jasmet.2023.v4i1.4527

Refbacks

  • There are currently no refbacks.


Copyright (c) 2023 Erifive Pranatal, Noveta Fernaldinatan, Norita Prasetya Wardhani

Creative Commons License
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.

Mailing Address: Journal of Applied Sciences, Management and Engineering Technology - ITATS Institut Teknologi Adhi Tama Surabaya Jl. Arief Rahman Hakim No.100, Surabaya 60117 email: [email protected] Website : https://ejurnal.itats.ac.id/jasmet/index Creative Commons License
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.